HB-RSLD
Neoprene heat shrink tubing HB-RSLD, resistant to oils and most types of solvents, including kerasin. After shrinkage, it also performs mechanical protection tasks. Used in rocketry, aviation, oil production.
Operating temperature: -55 ℃ to 135 ℃
Shrinkage temperature: 90 ℃ - 130 ℃
Colors: black
| Technical Data Property |
Test Method | Standard Value |
| Tensile Strength | ASTM D 412 | ≥10.3MPa |
| Elongation at Break | ASTM D 412 | ≥225% |
| Tensile Strength at 200% elongation | ASTM D 412 | ≤10.3MPa |
| Tensile Strength After Aging（120℃，168hrs） | SAE-AMS-DTL-23053 | ≥8.3MPa |
| Elongation at Break After Aging（120℃，168hrs） | SAE-AMS-DTL-23053 | ≥175% |
| Dielectric Strength | ASTM D 2671 | ≥11.8kV/mm |
| Volume Resistivity | ASTM D 876 | ≥1x1011Ω.cm |
| Flammability (Self extinguishing 15seconds;3inches） | ASTM D2671,Procedure A | Pass |
| Fungus resistance | ASTM G 21 | No growth |
| Low temperature flexibility | -70℃,4 hrs | No cracking |
| Recovered/mm | |||
| ID | As Supplied /mm | Inner Diameter | Wall thickness |
| HB-RSLD-3,2/1,5 | ≥3,2 | ≤1,5 | 0,7±0,2 |
| HB-RSLD-4,8/2,5 | ≥4,8 | ≤2,5 | 0,8±0,2 |
| HB-RSLD-6,4/3,4 | ≥6,4 | ≤3,4 | 0,9±0,2 |
| HB-RSLD-9,5/5,4 | ≥9,5 | ≤5,4 | 1,0±0,2 |
| HB-RSLD-12,7/7,1 | ≥12,7 | ≤7,1 | 1,2±0,3 |
| HB-RSLD-16/8,7 | ≥16 | ≤8,7 | 1,3±0,3 |
| HB-RSLD-19,1/10,5 | ≥19,1 | ≤10,5 ≤12,5 |
1,4±0,3 1,7±0,3 |
| HB-RSLD-22,2/12,5 | ≥22,2 | ≤14,5 | 1,8±0,3 |
| HB-RSLD-25,4/14,5 | ≥25,4 | ≤18,0 | 2,2±0,3 |
| HB-RSLD-31,8/18,0 | ≥31,8 | 2,3±0,3 | |
| HB-RSLD-38,1/21,5 | ≥38,1 | ≤21,5 | 2,4±0,3 |
| HB-RSLD-44,5/24 | ≥44,5 | ≤24,0 | 2,4±0,3 |